CHEMICAL COMPOSITION OF STAINLESS STEEL WIRE

Type AISI W.Nr JIS BSI AFONR UNI Range C% Mn% P% S% Si% Cr% Ni% Cu% Mo% Ti%
201 (Ni%:0.30)   -  -  -  -  -  Min -  7.00  -  -  -  13.00  0.30  1.50  -  - 
Max 0.15  9.50  0.075  0.030  1.00  16.00  0.50  2.50  0.30 
201 (Ni%:0.60)  -  -  -  -  -  Min -  7.00  -  -  -  13.00  0.50  1.50  -  - 
Max 0.15  9.50  0.100  0.030  1.00  16.00  0.70  2.50  0.30 
201 (Ni%:0.90)  -  -  Min  -  -  Min -  7.00  -  -  -  13.00  0.90  1.50  -  - 
Max 0.15  9.50  0.100  0.030  1.00  16.00  1.20  2.50  0.30 
201 (Ni%:3.00)  -  -  -  -  -  Min -  7.00  -  -  -  14.00  3.00  1.50  -  - 
Max 0.15  9.00  0.100  0.030  1.00  16.00  4.00  2.50  0.30 
202  -  -  Min  -  -  Min -  7.00  -  -  -  14.00  3.50  0.90  -  - 
Max 0.15  10.00  0.090  0.030  1.00  17.50  4.10  0.90  - 
204CU  -  -  -  -  -  Min -  6.5  -  -  -  14.0  1.50  1.50  -  - 
Max 0.15  8.5  1.00  0.03  2.00  17.0  3.00  2.50  - 
302  1.4310  SUS302  302S17  Z 12CN 17-07  X12CrNi 1707  Min -  -  -  -  -  17.00  8.00  -  -  - 
Max 0.15  2.00  0.045  0.030  1.00  19.00  10.00  -  - 
302HQ  1.4567  -  394S17  Z 2CN4 18-10  XM-7  Min -  -  -  -  -  17.00  9.00  3.00  -  - 
Max 0.30  2.00  0.045  0.030  1.00  19.00  11.00  4.00  - 
303  1.4305  SUS303  303S31  Z 10CNF 18-09  X10CrNi S1809  Min -  -  -  0.15  -  17.00  8.00  -  -  - 
Max 0.100  2.00  0.045  0.35  1.00  19.00  10.00  0.75  0.75 
304HC  -  -  -  -  -  Min -  0.80  -  -  0.30  18.00  8.0  2.00  -  - 
Max 0.045  2.00  0.045  0.030  1.00  20.00  10.5  3.00  - 
304Cu  -  -  -  -  -  Min -  -  -  -  -  17.00  8.0  3.00  -  - 
Max 0.040  2.00  0.045  0.030  1.00  19.00  10.5  4.00  - 
304  1.4301  SUS304  304S15  Z 6CN 18-09  X5CrNi 1810  Min -  -  -  -  -  18.00  8.00  -  -  - 
Max 0.08  2.00  0.050  0.030  1.00  20.00  10.50  -  - 
304L 1.4306 SUS304L 304S11 Z 2CN 18-10  X2CrNi 1811  Min -  -  -  -  -  18.00  8.00  -  -  - 
Max 0.03  2.00  0.050  0.030  1.00  20.00  10.50  -  - 
305  1.4303  -  -  -  -  Min -  -  -  -  -  17.0  11.0  -  -  - 
Max 0.060  2.00  0.045  0.030  1.00  19.0  13.0  -  - 
310S  1.4845  -  -  -  -  Min -  -  -  -  -  24.00  19.00  -  -  - 
Max 0.80  2.00  0.045  0.040  0.60  26.00  22.00  0.75  - 
314  1.4841  -  -  -  -  Min -  -  -  -  1.50  23.00  19.00  -  -  - 
Max 0.25  2.00  0.045  0.030  3.00  26.00  23.50  0.75  - 
316  1.4401  SUS316  316S31  Z 6CND 17-11  X8CrNiMo 1713  Min -  -  -  -  -  16.00  10.00  -  2.00  - 
Max 0.06  2.00  0.050  0.030  1.00  18.00  14.00  -  3.00 
316L  1.4404  SUS316L  316S11  Z 2CND 17-12  X2CrNiMo 17-12  Min -  -  -  -  -  16.00  10.00  -  2.00  - 
Max 0.03  2.00  0.050  0.030  1.00  18.00  14.00  -  3.00 
316Ti  1.4571  -  320S31- 320S17  Z 6CNDT 17-12  X6CrNiMoTi 1712  Min -  -  -  -  -  16.00  10.00  -  2.00  5xC%-0.80 
Max 0.080  2.00  0.0450  0.030  1.00  18.00  12.00  -  3.00 
321  1.4541  SUS321  321S31  Z 6CNT 18-10  X6CrNiTi 18-11  Min -  -  -  -  0.40  17.00  9.00  -  -  5 x C% 
Max 0.06  2.00  0.45  0.010  0.60  19.00  9.60  -  - 
410  1.4006  SUS410  410S21  Z 12C13  X12CM3  Min -  -  -  -  -  11.50  -  -  -  - 
Max -  1.00  0.040  0.030  1.00  13.50  -  -  - 
420  1.4034  SUS420  420S45  Z 30C13  X30Cr13  Min 0.15  -  -  -  -  12.00  -  -  -  - 
Max 0.25  1.00  0.040  0.030  1.00  14.00  -  -  - 
430  1.4016  SUS430  430S17  Z 8C17  X8Cr17  Min -  -  -  -  -  16.00  -  -  -  - 
Max 0.100  1.00  0.040  0.030  0.75  18.00  -  -  - 
430L  -  -  -  -  -  Min -  -  -  -  -  16.00  -  -  -  - 
Max 0.03  1.00  0.040  0.030  1.00  18.00  0.50  -  0.50 
434  -  -  -  -  -  Min -  -  -  -  -  16.00  -  -  0.75  - 
Max 0.12  1.00  0.040  0.030  1.00  18.00  0.40  0.70  1.25 
434A  -  -  -  -  -  Min -  0.30  -  -  -  16.00  -  0.60  -  - 
Max 0.10  0.60  0.040  0.015  0.70  18.00  0.40  1.00  0.20 
ER304L  -  -  -  -  -  Min -  1.50  -  -  -  18.00  9.00  -  -  - 
Max -  2.50  0.025  0.010  0.50  20.00  10.00  -  - 
ER308  -  -  -  -  -  Min -  -  -  -  0.30  19.00  9.00  -  - 
Max -  2.50  0.020  0.030  0.65  21.00  11.00  -  - 
ER308L  1.4331  -  308S92  Z 2CNS 20-10  -  Min -  1.50  -  -  -  19.0  9.00  -  -  - 
Max -  -  0.025  0.020  0.50  21.0  11.0  -  - 
ER309  -  -  -  -  -  Min -  1.00  -  -  0.30  23.0  12.0  -  -  - 
Max 0.10  2.50  0.025  0.025  0.65  25.0  14.0  -  - 
ER309L  1.4332  -  309S94  -  -  Min -  1.50  -  -  -  23.0  12.0  -  -  - 
Max -  2.50  0.020  0.015  0.60  24.0  14.0  -  - 
ER310  1.4842  -  310S94  Z 12CN 25-20  -  Min -  -  -  -  -  24.0  19.00  -  -  - 
Max 0.100  2.50  0.025  0.040  0.60  26.0  22.00  -  - 
ER312  1.4337  -  312S94  -  -  Min -  -  -  -  0.30  29.0  8.00  -  -  - 
Max 0.15  2.00  0.025  0.025  0.65  32.0  10.00  -  - 
ER316  -  -  -  -  -  Min -  -  -  -  0.30  18.00  12.0  -  2.00  - 
Max 0.080  2.00  0.025  0.025  0.65  20.00  14.0  -  3.00 
ER316L  1.4430  -  316S92  Z 2CND 19-13  -  Min -  -  -  -  -  18.0  11.00  -  2.00  - 
Max 0.025  2.00  0.023  0.015  0.65  20.0  14.0  -  2.50